Welcome to Baoding Donghe New Material Technology CO.,Ltd

SERVICE HOTLINE:

+86-312-7678999

  • NYBANNER

    NYBANNER

  • neiye

    neiye

  • nybanner

    nybanner

Online customer service
Customer service hotline
0312-7678999
Customer service team:
在线客服
Service time:
8:00 - 24:00

Mobile phone website

Baoding Donghe New Material Technology CO.,Ltd


Adress:Shunping County, Baoding City, Hebei Province
Telephone:+86-312-7678999  / 7678066  /  7678333
Cell phone:+86-15732221111   +86-13931375075
Fax:+86-312-7678222

Official station:http://www.bddonghekeji.cn
Ali Baba:http://donghesuye.1688.com
Email:dongheplastics@163.com
 

 

 

Watch for microsignals

Copyright © 2018  Baoding Donghe New Material Technology CO.,Ltd All Rights Reserved 冀ICP备13015991号  Powered by www.300.cn

>
News
>
>
Development of high-temperature resistant nylon engineering plastics in China --
Company News
Latest announcement
Industry News

Development of high-temperature resistant nylon engineering plastics in China --

[Abstract]:
  High temperature resistant nylon is a kind of nylon engineering plastic which can be used at 150 ℃ for a long time. It is a new type of special engineering plastic developed over the past ten years.
  High temperature resistant nylon is a kind of nylon engineering plastic which can be used at 150 ℃ for a long time. It is a new type of special engineering plastic developed over the past ten years. PA46 is the DSM company announced in 1984 to determine the industrial route, in 1985 to build 150 tons of mid-year pilot equipment, in 1990 to build a kilotons of industrial equipment. PPA46 is formed by condensation of butylamine and adipic acid. Because of its high symmetry, high crystal speed and perfect crystal. The HDT of PA46 can reach 150 ℃ and 285 ℃ after glass fiber enhancement. Dingere industrialization technology is the key technology of PA46, currently only the DSM master. Pvc panel PP panel plastic panel PP sheet
  Semi-aromatic nylon(PPAs) is a condensation of aromatic diacid and fatty diamine, with excellent properties between aromatic polyamide and fatty polyamide, and is nearly